High resilience (low-pressure variable) fluorosilicone rubber ALD-D-G10 series
1. Translucent or milky white high-resilience fluorosilicone compound rubber, with good physical properties and processing properties, has the characteristics of good resilience, low-pressure change, fast vulcanization speed, and good fluidity, and is more suitable for production Seal products.
2. How to use: Mixing: First, remix several times on the open mill, add a vulcanizing agent, and then adjust back to 0.5mm-1mm thin pass 8-10 times after eating the material, and then leave the film and park it.
Vulcanization: The mixed rubber with the vulcanizing agent added is re-milled, and then it is sliced or cut into the desired shape, and then molded and vulcanized on the molding machine.
3. Storage method: store in a dry environment at room temperature, valid for one year.
Description
| Reference fuel C strength change (%) (23℃x2h)Model | G1030 | G1040 | G1050 | G1060 | G1070 | G1080 | |
| Appearance | visual inspection | Translucent or off-white, smooth surface, no impurities | |||||
| Hardness (Shore A) | ASTMD240 | 30±5 | 40±5 | 50±5 | 60±5 | 70±5 | 80±5 |
| Tensile strength (MPa)Die C | ASTMD12 | 9.5 | 10.2 | 10.2 | 10.2 | 10.2 | 8.9 |
| Elongation at break (%)DieC | ASTMD12 | 430 | 410 | 355 | 332 | 270 | 205 |
| Tear strength (KNmDieB | ASTMD24 | 16 | 17 | 17 | 18 | 18 | 17 |
| Compression set 177℃ 22hr25%) Type B | ASTMD95 | 6.0 | 6.1 | 6.1 | 6.3 | 6.8 | 6.9 |
| Vertical resilience (%) | ASTMD632 | 31 | 31 | 32 | 32 | 32 | 32 |
| Reference fuel C volume change (%) (23℃x2h) | ASTMD471 | 17 | 17 | 17 | 17 | 17 | 17 |
| Reference fuel C strength change (%) (23℃x2h) | ASTMD471 | -20 | -20 | -20 | -20 | -20 | -20 |
| Reference fuel oil C elongation change (%) (23℃x2h) | ASTMD471 | -20 | -20 | -20 | -20 | -20 | -20 |
| Heat aging resistance strength change rate (%) (225℃x2h) | ASTMD573 | -17 | -17 | -17 | -17 | -17 | -17 |
| Heat aging resistance elongation rate (%) (225℃x2h) | ASTMD573 | -10 | -10 | -10 | -10 | -10 | -10 |