Common Silicone Rubber for Molding and Extrusion
Applications：
● Keypads, sealing rings, and sealing gaskets.
Typical Data：
●Physical data in the above table is for reference only.
●Vulcanization condition: 175℃* 5Min.
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di (tert- butyl peroxy) hexane: 0.65%.
● The Quality Inspection Department obtains the supplied test report with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee on the effectiveness or general applicability of our products under a particular application.
Description
| Properties | Product Data | Test Method | |||||||
| NE-7125 | NE-7130 | NE-7140 | NE-7150 | NE-7160 | NE-7170 | NE-7180 | NE-7190 | ||
| Appearance | Milk-white, light yellow,no obvious extraneous matter. | Visual Inspection | |||||||
| Density, g/cm3 | 1.05～1.10 | 1.07～1.11 | 1.10～1.14 | 1.13～1.17 | 1.16～1.20 | 1.19～1.23 | 1.20～1.24 | 1.21～1.25 | ASTMD792 |
| Hardness, Shore A | 25±2 | 30±2 | 40±2 | 50±2 | 60±2 | 70±2 | 80±2 | 86±2 | ASTMD2240 |
| Tensile Strength, MPa ≥ | 3.5 | 6.0 | 6.5 | 7.5 | 7.0 | 4.0 | ASTMD412 | ||
| Elongation at Break, % ≥ | 700 | 500 | 420 | 320 | 280 | 200 | 150 | 80 | |
| Tension Set, % ≤ | 8 | 7 | 8 | 7 | 6 | ||||
| Tear Strength, Die C kN/m ≥ | 10 | 15 | 16 | 18 | 17 | 16 | 10 | ASTMD624 | |
| Compression Set,180℃*22h ≤ | / | 50 | 30 | ASTM D395 | |||||
| Resilience, % ≥ | / | 60 | 50 | 45 | 40 | / | |||
| First-order linear shrinkage,% | 3.6～4.2 | 3.4～3.9 | 3.3～3.8 | 3.2～3.7 | 3.1～3.6 | 2.9～3.5 | 2.8～3.4 | 2.7～3.4 | / |