Self-lubricating Silicone Rubber
Applications：
●Automotive industry, machinery industry, and aerospace industry, such as various silicone rubber connectors, sealing elements, and washers requiring self-lubricating properties with molding process.
●Physical data in the above table is for reference only.
●Vulcanization condition: 175℃* 5Min.
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 0.65%.
● The Quality Inspection Department obtains the supplied test report with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee on the effectiveness or general applicability of our products under a specific application.
Description
| Properties | Product Data | Test Method | ||||||
| NE-1130 | NE-1140 | NE-1150 | NE-1160 | NE-1170 | ||||
| Appearance | Milk-white, no obvious extraneous matter. | VisualInspection | ||||||
| Density, g/cm3 | 1.03～1.13 | 1.08～1.18 | 1.10～1.20 | 1.14～1.24 | 1.17～1.27 | ASTM D792 | ||
| Hardness, Shore A | 30±2 | 40±2 | 50±2 | 60±2 | 70±2 | ASTM D2240 | ||
| Tensile Strength, MPa ≥ | 6.5 | 7.5 | ASTM D412 | |||||
| Elongation at Break, % ≥ | 600 | 500 | 350 | 300 | 220 | |||
| Tension Set, % ≤ | 8 | |||||||
| Tear Strength, Die C kN/m ≥ | 15 | 19 | 22 | 20 | ASTM D624 | |||
| Properties | Product Data | Test Method | ||||
| NE-1230 | NE-1240 | NE-1250 | NE-1260 | NE-1270 | ||
| Appearance | Milk-white, no obvious extraneous matter. | VisualInspection | ||||
| Density, g/cm3 | 1.03～1.11 | 1.09～1.17 | 1.11～1.19 | 1.14～1.22 | 1.18～1.26 | ASTM D792 |
| Hardness, Shore A | 32±2 | 40±2 | 50±2 | 60±2 | 70±2 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 6.5 | 8.0 | 7.5 | ASTM D412 | ||
| Elongation at Break, % ≥ | 700 | 600 | 500 | 400 | 300 | |
| Tension Set, % ≤ | 8 | |||||
| Tear Strength, Die C kN/m ≥ | 20 | 30 | 35 | ASTM D624 | ||
| Properties | Product Data | Test Method | |||||
| NE-1320 | NE-1330 | NE-1340 | NE-1350 | NE-1360 | NE-1370 | ||
| Appearance | Milk-white, no obvious extraneous matter. | VisualInspection | |||||
| Density, g/cm3 | 1.05～1.13 | 1.06～1.13 | 1.10～1.17 | 1.12～1.19 | 1.15～1.22 | 1.17～1.25 | ASTM D792 |
| Hardness, Shore A | 20±2 | 30±2 | 40±2 | 50±2 | 60±2 | 70±2 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 3.0 | 6.0 | 6.5 | 7.0 | ASTM D412 | ||
| Elongation at Break, % ≥ | 700 | 550 | 450 | 350 | 300 | 220 | |
| Tension Set, % ≤ | 8 | ||||||
| Tear Strength, Die C kN/m≥ | 10 | 15 | 19 | 22 | 20 | ASTM D624 | |