Fire Resistant Silicone Rubber

Fire Resistant Silicone Rubber

 

Applications:

●They are applicable to the manufacturing of electronic and electric products with flame retardant and insulative, such as flame retardant gaskets, flame retardant seal rings, and wire sheaths for cold cathode fluorescent lamps.

●Physical data in the above table is for reference only.

●Vulcanization condition: 175℃* 5Min.

●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 1.0%.

●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a certain application.

worldstrongsz@gmail.com 的头像

关于作者


热门分类


有用的链接

我发现了一些有用的链接,希望与大家分享。


搜索本站

Fire Resistant Silicone Rubber

 

Applications:

●They are applicable to the manufacturing of electronic and electric products with flame retardant and insulative, such as flame retardant gaskets, flame retardant seal rings, and wire sheaths for cold cathode fluorescent lamps.

●Physical data in the above table is for reference only.

●Vulcanization condition: 175℃* 5Min.

●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 1.0%.

●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a certain application.

Description

PropertiesProduct DataTest Method
NE-Z130NE-Z140NE-Z150NE-Z160NE-Z170NE-Z180
AppearanceWhite, no obvious extraneous matter.Visual Inspection
Density,  g/cm31.32~1.381.37~1.431.40~1.461.42~1.481.45~1.511.47~1.53ASTM D792
Hardness,  Shore A32±240±350±360±370±378±3ASTM D2240
Tensile Strength,  MPa   ≥3.54.56.05.5ASTM D412
Elongation at Break,  %  ≥400330280200170
Tension Set,  %        ≤68765
Tear Strength, Die C  kN/m ≥12131513ASTM D624
Flame Retardancy, 3mmFV-0IEC 60695-11-10
PropertiesProduct DataTest Method
NE-Z141NE-Z151NE-Z161NE-Z171
AppearanceWhite, no obvious extraneous matter.Visual Inspection
Density,  g/cm31.34~1.401.38~1.441.40~1.461.44~1.50ASTM D792
Hardness,  Shore A40±350±360±370±3ASTM D2240
Tensile Strength,  MPa   ≥5.06.05.5ASTM D412
Elongation at Break,  %  ≥400350300220
Tension Set,  %        ≤876
Tear Strength, Die C  kN/m  ≥131513ASTM D624
Flame Retardancy, 3mmFV-0IEC 60695-11-10
PropertiesProduct DataTest Method
NE-Z250NE-Z260NE-Z270NE-Z280
AppearanceWhite, no obvious extraneous matter.Visual Inspection
Density,  g/cm31.40~1.461.42~1.481.45~1.511.47~1.53ASTM D792
Hardness,  Shore A50±360±370±380±3ASTM D2240
Tensile Strength,  MPa  ≥6.05.54.5ASTM D412
Elongation at Break,  % ≥330280220180
Tension Set, %       ≤1210
Tear Strength, Die C  kN/m ≥1513ASTM D624
Flame Retardancy, 3mmFV-0IEC 60695-11-10
PropertiesProduct DataTest Method
NE-Z540NE-Z550NE-Z560NE-Z570NE-Z580
AppearanceWhite, no obvious extraneous matter.Visual Inspection
Density,  g/cm31.37~1.431.40~1.461.42~1.481.45~1.511.47~1.53ASTM D792
Hardness,  Shore A40±350±360±370±378±3ASTM D2240
Tensile Strength,  MPa  ≥4.05.0ASTM D412
Elongation at Break,  %   ≥350300250200150
Tension Set,  %       ≤8765
Tear Strength, Die C  kN/m ≥121412ASTM D624
Flame Retardancy, 3mmFV-0IEC60695-11-10