High-strength Silicone Rubber for Molding
Applications:
●They are applicable to the molding process and silicone rubber products with high requirements for tensile property and elongation rate.
●Physical data in the above table is for reference only.
●Vulcanization condition: 175℃* 5Min.
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 0.65%.
● The Quality Inspection Department obtains the supplied test report with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a particular application.
Description
Properties | Product Data | TestMethod | |||||
NE-8131 | NE-8135 | NE-8141 | NE-8151 | NE-8161 | NE-8171 | ||
Appearance | Milk-white, translucent,no obvious extraneous matter. | VisualInspection | |||||
Density, g/cm3 | 1.06~1.10 | 1.07~1.12 | 1.10~1.15 | 1.13~1.18 | 1.15~1.20 | 1.18~1.23 | ASTM D792 |
Hardness, Shore A | 30±2 | 35±2 | 40±2 | 50±2 | 60±2 | 70±2 | ASTM D2240 |
Tensile Strength, MPa ≥ | 6.0 | 6.5 | 7.5 | 9.0 | 8.5 | 7.5 | ASTM D412 |
Elongation at Break, % ≥ | 600 | 550 | 460 | 420 | 260 | ||
Tension Set, % ≤ | 6 | 7 | 8 | 7 | |||
Tear Strength, Die C kN/m ≥ | 15 | 17 | 20 | 24 | 22 | ASTM D624 | |
Compression Set, 180℃*22h ≤ | 35 | 30 | ASTM D395 | ||||
Rebound Resilience, % ≥ | 65 | 60 | 55 | 50 | 45 | / |