●Physical data in the above table is for reference only.
●Vulcanization condition: 175℃*5Min.
●Post-curing condition:200℃* 4h
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 0.65%.
● The Quality Inspection Department obtains the supplied test report with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a specific application.
Standard Fumed Silicone Rubber for Extrusion
Applications:
●Transparent silicone tubes & E-tubes and wire rods with a smooth surface
Description
Properties | Product Data | Test Method | |||||
NE-9240 | NE-9250 | NE-9260 | NE-9270 | NE-9280 | |||
Appearance | Transparent,no extraneous matter. | Visual Inspection | |||||
Density, g/cm3 | 1.09~1.15 | 1.12~1.18 | 1.14~1.20 | 1.17~1.23 | 1.18~1.25 | ASTM D792 | |
Curing | Hardness, Shore A | 40±2 | 50±2 | 60±2 | 70±2 | 80±2 | ASTM D2240 |
Tensile Strength, MPa ≥ | 8.0 | 8.5 | 8.0 | ASTM D412 | |||
Elongation at Break, % ≥ | 600 | 500 | 400 | 300 | 200 | ||
Tension Set, % ≤ | 8 | ||||||
Tear Strength , Die C kN/m ≥ | 20 | 25 | 20 | ASTM D624 | |||
Post-curing | Hardness, Shore A | 45±2 | 57±2 | 68±2 | 76±2 | 85±2 | ASTM D2240 |
Tensile Strength, MPa ≥ | 7.5 | 8.5 | 8.0 | ASTM D412 | |||
Elongation at Break, % ≥ | 520 | 450 | 340 | 260 | 200 | ||
Tear Strength, Die C kN/m ≥ | 18 | 20 | 18 | ASTM D624 | |||
Compression Set, 180℃*22h ≤ | 45 | 35 | 25 | ASTM D395 | |||
Rebound Resilience, % ≥ | 60 | 50 | 45 | 40 | / | ||
Volume Resistivity, Ω ▪cm ≥ | 1×1015 | IEC 60093 | |||||
Dielectric Strength, kV/mm ≥ | 20 | IEC 60243 |