Fire Resistant Silicone Rubber
Applications:
●They are applicable to the manufacturing of electronic and electric products with flame retardant and insulative, such as flame retardant gaskets, flame retardant seal rings, and wire sheaths for cold cathode fluorescent lamps.
●Physical data in the above table is for reference only.
●Vulcanization condition: 175℃* 5Min.
●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 1.0%.
●The supplied test report is obtained by the Quality Inspection Department with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a certain application.
Description
| Properties | Product Data | Test Method | |||||
| NE-Z130 | NE-Z140 | NE-Z150 | NE-Z160 | NE-Z170 | NE-Z180 | ||
| Appearance | White, no obvious extraneous matter. | Visual Inspection | |||||
| Density, g/cm3 | 1.32～1.38 | 1.37～1.43 | 1.40～1.46 | 1.42～1.48 | 1.45～1.51 | 1.47～1.53 | ASTM D792 |
| Hardness, Shore A | 32±2 | 40±3 | 50±3 | 60±3 | 70±3 | 78±3 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 3.5 | 4.5 | 6.0 | 5.5 | ASTM D412 | ||
| Elongation at Break, % ≥ | 400 | 330 | 280 | 200 | 170 | ||
| Tension Set, % ≤ | 6 | 8 | 7 | 6 | 5 | ||
| Tear Strength, Die C kN/m ≥ | 12 | 13 | 15 | 13 | ASTM D624 | ||
| Flame Retardancy, 3mm | FV-0 | IEC 60695-11-10 | |||||
| Properties | Product Data | Test Method | |||
| NE-Z141 | NE-Z151 | NE-Z161 | NE-Z171 | ||
| Appearance | White, no obvious extraneous matter. | Visual Inspection | |||
| Density, g/cm3 | 1.34～1.40 | 1.38～1.44 | 1.40～1.46 | 1.44～1.50 | ASTM D792 |
| Hardness, Shore A | 40±3 | 50±3 | 60±3 | 70±3 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 5.0 | 6.0 | 5.5 | ASTM D412 | |
| Elongation at Break, % ≥ | 400 | 350 | 300 | 220 | |
| Tension Set, % ≤ | 8 | 7 | 6 | ||
| Tear Strength, Die C kN/m ≥ | 13 | 15 | 13 | ASTM D624 | |
| Flame Retardancy, 3mm | FV-0 | IEC 60695-11-10 | |||
| Properties | Product Data | Test Method | |||
| NE-Z250 | NE-Z260 | NE-Z270 | NE-Z280 | ||
| Appearance | White, no obvious extraneous matter. | Visual Inspection | |||
| Density, g/cm3 | 1.40～1.46 | 1.42～1.48 | 1.45～1.51 | 1.47～1.53 | ASTM D792 |
| Hardness, Shore A | 50±3 | 60±3 | 70±3 | 80±3 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 6.0 | 5.5 | 4.5 | ASTM D412 | |
| Elongation at Break, % ≥ | 330 | 280 | 220 | 180 | |
| Tension Set, % ≤ | 12 | 10 | |||
| Tear Strength, Die C kN/m ≥ | 15 | 13 | ASTM D624 | ||
| Flame Retardancy, 3mm | FV-0 | IEC 60695-11-10 | |||
| Properties | Product Data | Test Method | ||||
| NE-Z540 | NE-Z550 | NE-Z560 | NE-Z570 | NE-Z580 | ||
| Appearance | White, no obvious extraneous matter. | Visual Inspection | ||||
| Density, g/cm3 | 1.37～1.43 | 1.40～1.46 | 1.42～1.48 | 1.45～1.51 | 1.47～1.53 | ASTM D792 |
| Hardness, Shore A | 40±3 | 50±3 | 60±3 | 70±3 | 78±3 | ASTM D2240 |
| Tensile Strength, MPa ≥ | 4.0 | 5.0 | ASTM D412 | |||
| Elongation at Break, % ≥ | 350 | 300 | 250 | 200 | 150 | |
| Tension Set, % ≤ | 8 | 7 | 6 | 5 | ||
| Tear Strength, Die C kN/m ≥ | 12 | 14 | 12 | ASTM D624 | ||
| Flame Retardancy, 3mm | FV-0 | IEC60695-11-10 | ||||