Standard Fumed Silicone Rubber for Extrusion

●Physical data in the above table is for reference only.

●Vulcanization condition: 175℃*5Min.

●Post-curing condition:200℃* 4h

●Ratio of curing agent liquid 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane: 0.65%.

● The Quality Inspection Department obtains the supplied test report with the curing conditions and testing method of the company; due to the difference in curing conditions and testing method, we can’t guarantee that both parties obtain the same testing result, and we suggest that users should use the test data obtained under their own testing conditions as the reference for service performance. All the above performance data and application recommendations are only a reference for use on the service performance of the product, instead of a guarantee of the effectiveness or general applicability of our products under a specific application.

Standard Fumed Silicone Rubber for Extrusion


●Transparent silicone tubes & E-tubes and wire rods with a smooth surface


PropertiesProduct DataTest Method
AppearanceTransparent,no extraneous matter.Visual Inspection
Density, g/cm31.09~1.151.12~1.181.14~1.201.17~1.231.18~1.25ASTM D792
CuringHardness, Shore A40±250±260±270±280±2ASTM D2240
Tensile Strength, MPa ≥ D412
Elongation at Break, %  ≥600500400300200
Tension Set,  %   ≤8
Tear Strength , Die C kN/m ≥202520ASTM D624
Post-curingHardness,  Shore A45±257±268±276±285±2ASTM D2240
Tensile Strength, MPa   ≥ D412
Elongation at Break, %   ≥520450340260200
Tear Strength, Die C kN/m ≥182018ASTM D624
Compression Set, 180℃*22h ≤453525ASTM D395
Rebound Resilience, %     ≥60504540/
Volume Resistivity,   Ω ▪cm   ≥1×1015IEC 60093
Dielectric Strength,  kV/mm   ≥20IEC 60243